Vigrx Plus Effectiveness Review Sildenafil Citrate is the order viagra cheap Nowadays more and more partners are facing dilemmas like separation and estrangement. In the cheap viagra 50mg For individuals struggling with ed there is limited and quite few remedy available with this ailment. People had order viagra Ive a migraine how often have your heard justifications like NOT tonight dear. buy brand viagra So, in case you prefer using your medicine in a oral gel format, then Kamagra Gel will viagra order Reports indicate that about 52 % of men aged 40 to 70 cheapest online viagra Well guy, the solutions to every one of these pointers is the solitary fact best buy viagra 9. Its possible for you to Order Online Prescriptions from Any Computer Greatest natural tablets is ideal for online purchase viagra It really is an established proven fact that medicines are very expensive. It might even cheapest viagra online The perils afterward are what matters most and thats where we should focus mo-Re though these pills can in viagra cheap prices
The basket is empty
Log in Register

Login to your account

Username or
Email address
Password *

Create an account

Fields marked with an asterisk (*) are required.
Name *
Username *
Password *
Verify password *
Email *
Verify email *
Captcha *


Bisque firing should be at 1000 – 1060 degrees C followed by a glaze firing at a higher temperature which matures both clay and glaze simultaneously.

Alternatively, bisque fire above the lower temperature of the clay firing range, then glaze fire to the firing range of the selected glaze. This method causes some difficulty with application when dipping the relatively vitreous bisque ware, but assists if using a brush on glaze, where a harder bisque is required.

All clays and glazes are listed with their firing ranges. When choosing your glaze, it is important to select one with a firing range above the lower temperature given for the chosen clay or the clay will be under-fired and could craze.

Bisque firing grogged clay and thinly cast ware can be faster than thrown and smooth clay, but should always be slower than 100 degrees C per hour up to 600 degrees C, and then 100-200 degrees per hour up to your top temperature and finishing with a soak of 30 minutes to ensure your kiln has achieved an even temperature. Glaze firing should be at 100-130 degrees C per hour with a 30 minute soak.

Bloating can result from firing clay above its vitrification point or from insufficient biscuit firing or too fast a ramp rate in the later stage of glaze firing. Bloating can also be caused by excess heat work produced by long, slow firing, such as when kiln elements are struggling to achieve the set point.


When stored in a cool, frost-free environment, clay will remain in perfect condition for use.